ADMER QB520E

In the vast plastics industry, the choice of polymer is crucial in determining the performance and cost of the final product. This discussion will compare two kinds of polypropylene, Braskem Polypropylene RP 225M and ADMER QB520E, which are suited for different jobs. RP 225M, a medium-flow random copolymer, sees use in film applications because of its good optical clarity and slip. QB520E, on the other hand, is a unique maleic anhydride-grafted homopolymer PP-based adhesive resin focused on adhesive applications in multilayer structures. If you're looking for the right material for flexible packaging, textile applications, or composite structures, this comparison guide will provide clear insights to help you make an informed choice.   1. Core Performance Comparison: RP 225M vs QB520E 1.1 Flowability and Density Features Braskem RP 225M ADMER QB520E Emphasis/Differences Mel Flow Rate (MFR) 8.0 g/10 min 1.8g/10min RP 225M has higher flowability, suitable for thin-walled or high-speed extrusion processes (such as films); QB520E has lower flowability, which is beneficial for improving melt strength and adhesion. Density 0.902g/cm3 0.90g/cm3 Both have very similar densities, falling within the typical polypropylene density range. 1.2 Mechanical Strength and Rigidity Features Braskem RP 225M ADMER QB520E Emphasis/Differences Tensile Yield Strength 28 MPa 24 MPa RP 225M has a slight edge in tensile strength, which may provide better load-bearing capacity in single-layer flexible packaging. Flexural Modulus 900 MPa N/A / Cantilever Impact Strength 30 J/m 470 J/m2 QB520E exhibits extremely high impact strength, consistent with its application as an adhesive layer in bottles, sheets, etc., where high toughness is required to withstand impacts. Elongation at Break 12%(Yield) 280% (Fracture) QB520E's elongation at break is significantly higher than RP 225M's yield elongation, confirming its high toughness and flexibility, ideal properties for an adhesive resin.   2. In-Depth Application Analysis: Identifying Your Needs 2.1 Braskem RP 225M: Transparency, Sliding, and Heat Sealing RP 225M is a product tailored for single-layer flexible packaging and textile applications. Key Features: Excellent Optical Properties: As a random copolymer, it inherently possesses better transparency and gloss than homopolymers, meeting the demands of high-definition packaging. Excellent Sliding Properties (Low Coefficient of Friction): Contains sliding agents and anti-blocking agents to ensure smooth operation on high-speed packaging machinery, preventing film sticking. Good Heat Sealing Properties: The lower initial heat-sealing temperature (111°C) helps improve packaging efficiency. Suitable Applications: Various flexible packaging films (flat extruded and blown films) 1717, especially for inner or middle packaging requiring high transparency and ease of handling, as well as textile applications. 2.2 ADMER QB520E: The "Glue" for Multilayer Structures QB520E is essentially an adhesive resin designed to solve the problem of direct bonding between different polymer layers. Key Characteristics: Strong Bonding: Utilizing maleic anhydride grafting technology, it can form strong chemical bonds with polar materials (such as EVOH or PA (polyamide)) and non-polar PP substrates, creating a high-barrier, high-strength multilayer structure. High Toughness: Extremely high impact strength (470 J/m²) and elongation at break ensure that the composite material will not delaminate under impact or bending. Processing Stability: Maximum processing temperature up to 300°C provides safety for multilayer co-extrusion. Applications: Primarily used in co-extrusion processes as an adhesive between PP and EVOH/PA barrier layers. Typical products include: Multilayer Barrier Bottles and Sheets: Used for packaging with high barrier requirements, such as for food and cosmetics. Multilayer Blown Films and Pipes: Ensures the integrity and durability of pipe and high-barrier film structures.   3. Production and Safety Considerations 3.1 Processing Recommendations RP 225M: Use planar film extrusion or blown film extrusion processes. High MFR is beneficial for processing. QB520E: Although it has low flowability, it does not require pre-drying, simplifying preparation for multilayer co-extrusion processes. Its melt viscosity-shear rate profile (rheological profile) helps to precisely control layer thickness in co-extrusion. Attention should be paid to the maximum temperature limit (300°C) to avoid decomposition. 3.2 Safety and Regulations RP 225M: Not recommended for packaging or products that come into contact with parenteral solutions or the human body. QB520E: Regarding food contact conditions, its components have relevant compliance statements in the EU and US FDA (as an adhesive), but the manufacturer is responsible for ensuring that the final application complies with all food contact regulations.   4. Summary and Recommendations Your final choice depends on your product structure: If you need to manufacture a single-layer packaging film with good clarity, rigidity, and slip resistance, RP 225M is ideal. If you need to manufacture a multi-layered structure (such as plastic wrap or barrier bottles) that includes a barrier layer (such as Ethylene-VinylAlcohol Copolymer (EVOH) /PA), QB520E is a key material to ensure strong adhesion and high toughness between different layers.   Website: www.elephchem.com Whatsapp: (+)86 13851435272 E-mail: admin@elephchem.com